Templated carbon monolithic tubes with shaped micro-channels and method for making the same

ABSTRACT

Disclosed is a method for forming an article with template shaped channels by (a) mixing a precursor with a fibrous template, (b) forming the mixture into a pre-determined shape, (c) curing the mixture to form a precursor composite, (d) carbonizing the precursor composite, and (e) decomposing the fibrous template to yield a shaped carbon article with template shaped channels.

BACKGROUND OF THE INVENTION

Smoking articles, particularly cigarettes, generally comprise a tobaccorod of shredded tobacco (usually, in cut filler form) surrounded by apaper wrapper, and a cylindrical filter aligned in an end-to-endrelationship with the tobacco rod. Typically, the filter includes a plugof cellulose acetate tow attached to the tobacco rod by tipping paper.

Upon lighting a cigarette, a smoker draws mainstream smoke from the litend of the cigarette. The drawn cigarette smoke first enters theupstream end portion of the filter and then passes through thedownstream portion adjacent the buccal end of the cigarette, upon whichthe user draws the smoke.

To achieve appropriate filtration efficiency, materials such as carbonhave been incorporated into cigarette filters. A current method forincorporating adsorbent materials in cigarette filters is the physicalentrapment of adsorbent particles between cellulose acetate (CA) fibers.An improved and more expensive design is to put certain materials in thecavity between CA plugs in a predetermined configuration, such as aplug-space-plug filter configuration, to limit the exposure of adsorbentto the triacetin binder.

Certain cigarettes incorporate filter segments with adsorbent materialssuch as activated carbon to achieve desired filtering characteristics.Examples of such filters are described in U.S. Pat. Nos. 2,881,770 toTovey; 3,353,543 to Sproull et al.; 3,101,723 to Seligman et al.; and4,481,958 to Ranier et al. Certain commercially available filters haveparticles or granules of carbon (e.g., an activated carbon material)alone or dispersed within a CA tow. Other commercially available filtershave carbon threads dispersed therein; while still other commerciallyavailable filters have so-called “plug-space-plug”, “cavity filter” or“triple filter” designs. Examples of commercially available filters areSCS IV Dual Solid Charcoal Filter and Triple Solid Charcoal Filter fromFiltrona International, Ltd.; Triple Cavity Filter from Baumgartner; andACT from Filtrona International, Ltd. Detailed discussion of theproperties and composition of cigarettes and filters is found in U.S.Pat. Nos. 5,404,890 and 5,568,819, both to Gentry et al, the disclosuresof which are hereby incorporated by reference.

Cigarette filter elements which incorporate carbon have the ability toremove constituents of mainstream smoke that pass therethrough. Inparticular, activated carbon has the propensity to reduce the levels ofcertain gas phase components present in the mainstream smoke, resultingin a change in the organoleptic and toxicological properties of thatsmoke.

It would be desirable to provide a cigarette having a cigarette filterincorporating carbon and/or other materials capable of absorbing and/oradsorbing gas phase components present in mainstream cigarette smoke,while providing favorable absorption/adsorption, dilution and drawingcharacteristics, so as to enhance consumer acceptability.

Furthermore, commercially available activated carbons and molecularsieves are typically in granular and powdered forms. Materials in theseforms do not maintain product cohesion, as granules or grains tend tosettle after being packed inside a cigarette filter. It is thereforedesirable to form rod-shaped, channeled, activated carbon articles, suchas monolithic tubes, for use in cigarette filtration to achieve lowerresistance to draw, higher total particulate matter delivery, and betterproduct integrity.

SUMMARY OF THE INVENTION

According to a preferred embodiment of the invention, a method isprovided for mixing excess carbon precursor materials such as phenolicresins with fibrous templates made of low carbon yielding materials suchas polypropylene; forming the mixture into a predetermined shape, suchas by pulling the mixture through a paper, plastic, metal or glass tube;trimming the excess mixture or cutting the tube to form a cylindricalshape; curing the mixture in the tube to form a precursor composite witha stable shape; removing the tube; carbonizing the precursor compositeunder inert media or vacuum; and decomposing the fibrous templates toyield shaped carbon articles, such as monolithic tubes with shapedchannels.

Further according to a preferred embodiment of the invention, carbonmonolithic articles with shaped channels are provided and used to formfilters, and more particularly cigarette filters that are effective atreducing smoke gas phase components.

BRIEF DESCRIPTION OF THE FIGURES

Novel features and advantages of the present invention in addition tothose mentioned above will become apparent to persons of ordinary skillin the art from a reading of the following detailed description inconjunction with the accompanying drawings wherein similar referencecharacters refer to similar parts and in which:

FIG. 1 is a schematic diagram showing the steps to form a shapedchanneled cigarette filter according to the present invention;

FIG. 2 is a side elevational view of a cigarette with portions thereofbroken away to illustrate interior details including a plug-space-plugfilter with filter comprising a carbon article according to the presentinvention;

FIG. 3 illustrates the cross-section of a tri-lobal shaped fibroustemplate according to the present invention;

FIG. 4 illustrates the cross-section of a quadri-lobal shaped fibroustemplate according to the present invention;

FIG. 5 illustrates the cross-section of a V-shaped fibrous templateaccording to the present invention;

FIG. 6 illustrates the cross-section of nested stylized I-shaped fibroustemplates according to the present invention;

FIG. 7 illustrates the cross-section of a C shaped fibrous templateaccording to the present invention;

FIG. 7A illustrates the cross-section of a round fibrous templateaccording to the present invention;

FIG. 7B illustrates the cross-section of a tubular fibrous templateaccording to the present invention;

FIG. 8 illustrates the cross-section of an irregular shaped fibroustemplate according to the present invention;

FIG. 9 illustrates a puff-by-puff comparison between the performance ofthe 1R4F sample with a CA filter according to the prior art and acigarette with a filter prepared according to the present invention withregard to 1,3-butadiene delivery;

FIG. 10 illustrates a puff-by-puff comparison between the performance ofa 1R4F sample with a CA filter according to the prior art and acigarette with a filter prepared according to the present invention withregard to acetone delivery;

FIG. 11 illustrates a puff-by-puff comparison of performance of a 1R4Fsample with a CA filter according to the prior art and a cigarette witha filter prepared according to the present invention with regard tobenzene delivery; and

FIG. 12 illustrates a puff-by-puff comparison between the performance ofa 1R4F sample with a CA filter according to the prior art and acigarette with a filter prepared according to the present invention withregard to formaldehyde delivery.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT

FIGS. 1 and 2 illustrate examples of a process and a final productaccording to the present invention. It will be readily understood thatthe scope of this invention is not limited to these embodiments. Rather,the scope of the present invention includes alternatives thatincorporate the filter and method of making the filter described herein.

As shown in FIG. 1, a typical process suitable for the mixing step maystart with a fibrous template 10 with hollow channels 12. Fibroustemplate 10 may be made from a material that will leave an insignificantamount of residue upon thermal decomposition. Templates 10 may alsocomprise low carbon yielding materials. A preferred material for thispurpose is polypropylene (PP).

The fibrous template 10 can be formed with a cross-section of any ofvarious shapes including, but not limited to, trilobal shaped,quadri-lobal shaped, V-shaped, stylized I-shaped or nested stylizedI-shaped, C-shaped, round, tubular, and irregular shaped, as designatedby reference numerals 10 through 10G in FIGS. 3 through 8, respectively.The shapes can be formed through extrusion, spinning or other shapeforming process as taught, for example, in U.S. Pat. No. 5,057,368 toLargman et al. The cross-sectional shape of the template provideslongitudinal channels 12 that may be continuous and that open to thesurface of template 10. Longitudinal channels 12 may have a variety ofshapes depending on the template shape, as designated by referencenumerals 12A through 12E in FIGS. 3 through 8, respectively.

The fibrous template bundle can be mixed with a carbon precursor in acontainer (not shown) to form a precursor laden bundle 11. The mixingstep may be conducted in accord with well known techniques, such asdescribed in U.S. Pat. Nos. 6,584,979 and 5,772,768 to Xue et al.Additional methods are well known as taught for example in “HighlyEfficient Acid-Gas Removing Shaped Fiber Filters”, Fundamental andApplied Aspects of Chemically Modified Surfaces; The Royal Society ofChemistry; Ed. by C. Little and J. Blitz; page 154, 1999. Certain levelsof agitation or rotation of the container may be necessary to achievecontinuously homogeneous impregnation of templates 10 with precursor 18.

The carbon precursor materials used in the mixing step may be solidparticles, gels, liquids, foams or mixtures thereof, which yield carbonor carbonoid materials upon heating to an adequate temperature in aninert atmosphere or under vacuum. Suitable materials in these classesinclude, but are not limited to, phenolic resin, petroleum pitches,polyacrylonitrile, cellulose, cellulose derivatives, polyvinyl acetate(PVA) and their mixtures. Additional inorganic materials such asmolecular sieves, zeolites, and silicates may be included in the mixtureto modify the pore-distribution of the final carbonoid products. Thephenolic resins used can be uncured or partially cured Novolak typeswith the presence of curing agents, or Resole (self-curing) types ormixtures of these. The production of porous shaped phenolic based carbonmaterials from a comminuted partially cured resin is taught, forexample, in U.S. Pat. No. 4,917,835 to Lear et al.

Fibrous template 10 may be handled as a random bunch or bundle 11 or ina manner such that templates or template segments may or may not berelatively aligned. Bundle 11, which may comprise single or multiplefibers, is then pulled with carbon precursor 18 through a mold 14 withdefined dimensions, which is shown in FIG. 1, for example, as a tube.The mold may comprise paper, plastic, metal, or glass.

An amount of carbon precursor 18 may be included in the mixture so thattemplates 10 are integrated into a unified piece. Any voids, openings orannular spaces in the mold 14 may be filled with precursor 18. Theweight ratio of carbon precursor 18 to polypropylene template 10, alsocalled the loading factor, is preferably within, but not limited to, therange of 0.2-6.

Continuous impregnation processes using continuous rolls of templatefibers 10 can be used to accomplish similar results to the batchprocess. Templates 10 can be pulled continuously through the container(not shown) containing the carbon precursor 18, reassembled through acone-shaped guide (not shown) and integrated into a continuous mold (notshown) for further processing. Certain levels of agitation or rotationof the mold may be necessary to achieve continuously homogeneousimpregnation. U.S. application Ser. No. 10/294,346 entitled “ContinuousProcess for Impregnating Solid Adsorbent Particles into ShapedMicro-cavity Fibers and Fiber Filters” is hereby incorporated byreference in its entirety and describes exemplary processes forcontinuous processing and impregnation of fibrous templates.

After impregnating mold 14 with the mixture comprising template 10 andprecursor 18, excess templates 10 and/or precursor 18 of bundle 11 mayextend from the mold 14 as shown in FIG. 1. Blades 16 may be used toobtain desirable lengths as well as to remove any excess templates 10 ofbundle 11 or precursor 18 extending from mold 14.

Precursor 18 and template 10 are then cured to form composite 19. Tocure the mixture, conditions may be selected to maintain the integrityof the templates 10 while the carbon precursor 18 is cured inside themold. Curing conditions depend greatly on the components in carbonprecursor 18, especially the uncured components used as binders. Forexample, curing can be accomplished by heating in a controlledatmosphere at a temperature of approximately 120-160° C. forapproximately 15-60 minutes, though other temperatures and times areanticipated to be acceptable. A certain level of acid may be added tothe phenolic precursor to accelerate the curing. After curing, thecomposite may retain its shape even if mold 14 is removed.

The composite may then be carbonized. For example, composite 19 may beheated in an inert environment and/or under vacuum, which may decomposetemplate 10 and allow the composite 19 to a yield templated carbonarticle 21, such as a monolithic tube, with voids or channels 20.Carbonization temperatures can be selected based on the precursor used.For example, the temperature may be selected from the range of about600° C. to about 950° C., and is preferably approximately 850° C.Channels 20 derive their shapes from those of templates 10. As withcuring, conditions for the carbonization may vary based on thecomponents in carbon precursor 18.

Various carbon yields and configurations can be obtained using variousshapes and processing conditions. Table 1 lists seven examples conductedusing various template shapes and processing conditions to achievediffering resulting channels. For each of the examples, a polypropylenetemplate was mixed with a phenolic resin based carbon precursor.Templates of 16 and 24 denier per filament (dpf) were used withdiameters of approximately 60-120 micrometers. In Table 1, the diametersare listed as d1. In the case of the trilobal shape, the diameter isbased on the circular shape created by the cross-section. In the case ofc-shaped or irregular shaped templates, d1 is given by two numbers,which represent the relative extent of the cross-section in twoorthogonal directions. The templates were loaded into a mold with aloading factor of between 0.2 and 6. Curing took place at approximately150° C. for approximately 25 to 40 minutes. Upon curing, the compositeshad a diameter D1. A certain level of acid may be added to the phenolicprecursor to accelerate this curing time. Carbonizing was performed atapproximately 850° C. for approximately 1-2 hours. Upon carbonizing, thediameter of the article was reduced to D2. Carbon yields were generallyin the range of 30-40% by weight depending on the polypropylene contentof the composite precursor. The channels formed in the carbon articlesderived their shape from the shape of the template. The resultingdiameter of the channels was d2, while the resulting number of channelsper mm² is represented by N.

TABLE 1 Examples of Processing Conditions and Shapes and the FinalProduct Process Carbonizing/ Template Loading Curing/150° C. 850° C.C_Tube Channels Example Fiber d1/μm Factor Min. D1/mm Hour Yield % D2/mmShape d2/μm N/mm² 1 Trilobal- 80 1.3 25 8 2 32 6.5 Triad 100-143 16824dpf 2 Round- 61 2.7 40 8 2 32 6 R 28-50 207 24dpf 3 Round- 61 3.2 25 82 33 6 R n/a 168 24dpf 4 Trilobal- 80 4.8 35 8 2 36 5.5 Triad 48-65 16824dpf 5 C-24dpf 66X80 4.0 20 19 1 36 12 C 55-75 351 6 Irregular- 60X1205.6 40 8 2 40 4 4DG  66-120 322 16pdf 7 C-24dpf 66X80 3.5 30 19 1 33 12C 55-75 391

Templated carbon articles 21 can be activated to form high surface areaadsorptive materials for filtration applications. Many activationprocesses are known in the literature such as heating with carbondioxide or water steam. For example, the templated carbon article fromExample 7 in Table 1 can be activated with carbon dioxide at atemperature of 950° C. for approximately 40 minutes. At a 25% burn-offrate, a BET surface area of 1219 m²/g and a micro-pore volume (<20 A) of0.4469 cm³/g have been obtained. These values are comparable to those ofcoconut based activated carbon, which may also be used as adsorbent incigarette filters.

The carbon article can additionally be activated to enhance itsfiltering characteristics. For example, modified cigarette modelscontaining a 66 mg activated templated carbon article can be formedaccording to Example 5 from Table 1 and the carbon can then be activatedat a temperature of approximately 950° C. for approximately 30 minutesto achieve a burn-off rate of 30%. As shown in FIG. 2, the filters canbe arranged such that conventional plugs 22 and 24 surround templatedcarbon article 21 prepared according to the present invention. Thecigarettes can be smoked under FTC conditions and the smoke chemistryanalyzed by FTIR and GC/MS methods. As shown in Tables 2-3 and FIGS.9-12, the formed filters are effective at reducing a wide range of smokegas phase components.

Table 2 compares a standard 1R4F cigarette to a cigarette containing acarbon article according to the present invention with thecharacteristics described in Example 5 from Table 1. The KentuckyReference 1R4F is a filtered cigarette that has been provided by theTobacco and Health Research Institute, University of Kentucky over theyears for research purposes. The first row of Table 2 provides the TPMvalues of an 1R4F sample. The standard deviation is given with the 1R4Fdata. The second row of Table 2 lists the characteristics of modifiedsamples MT-66-1 and MT-66-2, which were made according to the presentinvention and which were provided as a percentage difference incharacteristics from the control sample 1R4F. Modified samples MT-66-1and MT-66-2 were cigarettes with the structure shown in FIG. 2 in whichplug 22 was 15 mm, plug 24 was 7 mm and the carbon article 26 was 5 mmin axial length and the carbon article weighed 66 mg, though any lengthsand/or weights could be selected.

The values reported for modified samples MT-66-1 and MT-66-2 are givenas a change from the 1R4F standard. A change of greater than three timesthe standard deviation of the 1R4F control sample is consideredsignificant. As shown in Table 2, the amount of acetaldehyde (AA),hydrogen cyanide (HCN), methanol (MEOH) and isoprene (ISOP) in the totalparticulate matter (TPM) all decreased as a result of employing thepresent invention.

TABLE 2 Characteristics of control cigarette compared to those ofmodified cigarettes. AA HCN MEOH ISOP TPM CF SAMPLE (TPM) (TPM) (TPM)(TPM) (mg) RTD (mg) 1R4F (TPM × 10⁻³) 51.5 9.2 6.2 23.7 13.3 140 0.0Standard Deviation    8%    4%    9%    8% 3% 5% Modified Sample MT-66-1−32% −34% −32% −40% 16.6 113 66 Modified Sample MT-66-2 −54% −32% −44%−38% 13.0 119 66

Table 3 further illustrates the benefits of the present invention. Thefirst column lists characteristics and components common to cigarettesand cigarette smoke. The second column, labeled “Control Sigma,” liststhe standard deviation of certain gas phase components present in acontrol 1R4F cigarette. The third column, labeled “MT-66”, lists thechanges in component gas levels as a result of using filters made inaccordance with the present invention, and more particularly Example 5from Table 1.

TABLE 3 Change in Gas Phase Components Adsorbent Control Runs SigmaMT-66 Carbon/mg  66 Reference# 9627-79 Gas phase components ChangeCarbon Dioxide 5% No significant change Ethane 6% No significant change1,3-Butadiene 8% −41% Isoprene 5% −37% Cyclopentadiene 5% −46%1,3-Cyclohexadiene 17%  −80% Methyl Cyclopentadiene 9% −84% Formaldehyde14%  −86% Acetone 12%  −79% Diacetyl 5% −93% Methyl ethyl ketone 4% −90%Isovaleraldehyde 9% −79% Benzene 8% −82% Toluene 7% −92% Butyronitrile8% −93% 2-Methylfuran 4% −67% 2,5-Dimethylfuran 5% −87% 1-Methylpyrrole8% −93% Ketene 11%  −85%

FIGS. 9-12 further illustrate how MT-66 modified samples reduce thepuff-by-puff delivery of 1,3-butadiene, acetone, benzene, andformaldehyde.

For example, FIG. 9 shows the average amount of 1,3-butadiene inmainstream smoke for different puffs from Kentucky reference IR4Fcigarettes. 1,3-Butadiene in cigarette smoke is measured on a per puffbasis. Cigarettes are smoked with a 35 cc puff volume of two secondduration, once every 60 seconds. The puff-by-puff 1,3-butadienedeliveries are reported for eight determinations of 1R4F as well as theMT-66 sample. As shown in FIG. 9, the first puff accounts for between 15and 20% of the total delivery of the 1R4F, but less than 5% for theMT-66 sample. The process is repeated seven more times according to wellknown and reported methods to obtain the graphs shown in FIGS. 9-12.

As shown in FIGS. 9, 10 and 11 the content the constituent gasesincreases each puff due to saturation of the filter. However, thecontent of formaldehyde, shown in FIG. 12, reduces to nearly zero forproducts incorporating the present invention.

The foregoing description of the invention illustrates and describes thepresent invention. Additionally, the disclosure shows and describes onlythe preferred embodiments of the invention, but it is to be understoodthat the invention is capable of use in various other combinations,modifications, and environments and is capable of changes ormodifications within the scope of the inventive concept as expressedherein, commensurate with the above teachings, and/or the skill orknowledge in the art of filter preparation and, more particularlycigarette filter preparation.

The embodiments described hereinabove are further intended to explainthe best modes known of practicing the invention and to enable othersskilled in the art to utilize the invention in such, or other,embodiments and with the various modifications required by theparticular applications or uses of the invention. Accordingly, thedescription is not intended to limit the invention to the form disclosedherein. Also, it is intended that the appended claims be construed toinclude alternative embodiments.

1-12. (canceled)
 13. An article for smoking comprising: a plug; a carbonarticle with template-shaped channels adjacent to the plug; and atobacco rod.
 14. The article of claim 13 wherein the template shapedchannels are trilobal shaped, quadri-lobal shaped, V-shaped, I-shaped,stylized I-shaped, C-shaped, round, tubular or irregular shaped.
 15. Acarbon article formed according to the method of claim
 1. 16. A carbonarticle with template-shaped channels.
 17. The carbon article of claim16 wherein the template-shaped channels are trilobal shaped,quadri-lobal shaped, V-shaped, I-shaped, stylized I-shaped, C-shaped,round, tubular or irregular shaped.
 18. The carbon article of claim 16,wherein the carbon article is a monolithic tube.